Strength of a Zirconia-Reinforced Lithium Silicate Ceramic: Acid-Etching Time and Resin Cement Application Effects.

07:03 LMT 1st January 0000 | BioPortfolio

Summary of "Strength of a Zirconia-Reinforced Lithium Silicate Ceramic: Acid-Etching Time and Resin Cement Application Effects."

This study aimed to evaluate the effect of hydrofluoric (HF)-acid-etching time and the impact of a resin-cement layer on the biaxial flexural strength and structural reliability of a zirconia-reinforced lithium silicate (ZLS) glass ceramic. Disc-shaped specimens (n = 15) were divided according to: etching time (conditioning with 10% HF acid for 20, 40, and 60 seconds), and application of a resin-cement layer. Biaxial flexural, contact angle, and roughness analyses were performed. When the resin-cement layer was not present, flexural strength data increased with increasing etching times: 20 seconds = 250.8 MPa; 40 seconds = 278.4 MPa; 60 seconds = 342.9 MPa. Application of resin cement increased the strength values (20 seconds of acid etching on specimens with a resin-cement layer = 341.8 MPa). Different etching times did not affect the roughness of ZLS, and the contact-angle analysis presented lower values for 60 seconds of acid etching. The flexural strength of ZLS was only sensitive to surface changes when less exposure time was conducted. Longer etching times (40 and 60 seconds) should be considered for conditioning ZLS ceramic along with adhesive cementation.


Journal Details

This article was published in the following journal.

Name: The International journal of periodontics & restorative dentistry
ISSN: 1945-3388
Pages: 431-437


DeepDyve research library

PubMed Articles [9664 Associated PubMed Articles listed on BioPortfolio]

Bond Strength Stability of Self-adhesive Resin Cement to Etched Vitrified Yttria-stabilized Tetragonal Zirconia Polycrystal Ceramic After Thermomechanical Cycling.

The purpose of this study was to evaluate the influence of thermomechanical cycling on the bond strength stability of self-adhesive resin cement to vitrified yttria-stabilized tetragonal zirconia poly...

Fracture Resistance of Titanium, Zirconia, and Ceramic-Reinforced Polyetheretherketone Implant Abutments Supporting CAD/CAM Monolithic Lithium Disilicate Ceramic Crowns After Aging.

The purpose of this study was to compare the fracture resistances and the fracture types of titanium, zirconia, and ceramic-reinforced polyetheretherketone (PEEK) implant abutments supporting CAD/CAM ...

Effect of Self-Etching Primer Associated to Hydrofluoric acid or Silane on Bonding to Lithium Disilicate.

To evaluate the effect of combining 5% hydrofluoric acid (HF) and silane (SI) with the self-etching ceramic primer on the immediate and after 1-year of water storage on bonding efficacy, conditioning ...

Response of pre-crystallized CAD/CAM zirconia-reinforced lithium silicate glass ceramic to cyclic nanoindentation.

This paper reports on a cyclic nanoindentation approach of a pre-crystallized zirconia-reinforced lithium silicate glass ceramic (ZLS) to understand its material behavior associated with its machinabi...

Adhesion to a Lithium Disilicate Glass Ceramic Etched with Hydrofluoric Acid at Distinct Concentrations.

This study evaluated the effect of different hydrofluoric acid (HF) concentrations on the bond strength between a lithium disilicate-based glass ceramic and a resin cement. Eighty ceramic-blocks (12×...

Clinical Trials [4835 Associated Clinical Trials listed on BioPortfolio]

Evaluation of Antagonist Wear Behavior and Patient Satisfaction of Zirconia Reinforced Lithium Silicate Glass When Compared to Monolithic Zirconia

evaluation of wear behavior and patient satisfaction of monolithic zirconia and zirconia reinforced glass crowns after follow-up periods 0,3,6,12 months.

Clinical Outcomes of Zirconia-reinforced Lithium Silicate Partial Coverage Crowns Compared to Lithium Disilicate Partial Coverage Crowns

The purpose of this randomized controlled clinical trial is to evaluate the clinical outcomes of Partial Coverage Restorations fabricated with zirconia-reinforced lithium silicate ceramic ...

Clini Asses of Pt Satisfactn,Retentn,Fracture&PD Health of Reinforced Lithium Silicate (RLS)Endocrs Versus Post RLS Crs

Patient satisfaction ,retention,fracture and periodontal health of endodontically treated teeth restored with Reinforced Lithium Silicate Endocrowns in comparison to Post Retained Reinforc...

Ceramic Tooth Restorations - a Comparison Study

This randomized clinical study aims to compare success and survival of two different ceramic tooth restoration materials. The hypothesis for the study is that fluoride treated zirconia wil...

Wear Characteristics and Clinical Performance of Lithium Silicate Versus Monolithic Zirconia Crowns.

The aim of the present study is to evaluate the wear characteristics and clinical performance of lithium silicate crowns in comparison to monolithic zirconia crowns. The quality of the ov...

Medical and Biotech [MESH] Definitions

Preparation of TOOTH surfaces and DENTAL MATERIALS with etching agents, usually phosphoric acid, to roughen the surface to increase adhesion or osteointegration.

A lithium salt, classified as a mood-stabilizing agent. Lithium ion alters the metabolism of BIOGENIC MONOAMINES in the CENTRAL NERVOUS SYSTEM, and affects multiple neurotransmission systems.

Preparation of TOOTH surfaces, and of materials bonded to teeth or DENTAL IMPLANTS, with agents and methods which roughen the surface to facilitate adhesion. Agents include phosphoric or other acids (ACID ETCHING, DENTAL) and methods include LASERS.

A salt of lithium that has been used experimentally as an immunomodulator.

Inorganic compounds that contain lithium as an integral part of the molecule.

Quick Search


DeepDyve research library

Searches Linking to this Article